Strengths of Alloy-TiC

  • Excellent Wear Resistance
    Excellent wear resistance is one of the most well-known strengths of Alloy-TiC, the particle of TiC (HRC92 rounded shape) after lapping and polishing is higher hardness than WC (30% or more) and coefficient of friction which result in minimizing the pick-up, galling and chipping during the contacting other materials and almost no wear loss
  • Low density of Alloy-TiC offers cost-down effect
    Density of Alloy-TiC(6.5g/cm3) is much lower than WC(14.5g/cm3) or Tool Steel(8g/cm3). Alloy-TiC is cheaper than other materials applying the same volume parts. Instead of WC, parts are lighter and reduce the cost of repair and change relatively.
  • Alloy-TiC is the only machinable carbide composite
    After annealing of Alloy-TiC, the hardness is HRC43-45, which is machinable normally, and after heat-treatment the hardness is HRC68-72 as well as the Coefficient of Thermal Expansion is stable (±0.00025mm/mm )
  • Alloy-TiC is zero defect sintered carbide composite
    By H.I.P process there is no holes inside


  • Finest rounded grains for better lubrication and local friction mode
  • Less wear on roller grooves, hence high output of the mill
  • No breakage / galling / chipping of rollers during rolling
  • Less stoke removal per re-grind, hence longer life
  • Uniformity and stability of the finished products
  • High resistance to oxidation and less material pick-up on surface
  • Reduced risk of bearing breakage and failure due to low density

Alloy-TiC Properties

Rupture Strength(KSI)
Impact Strength

Alloy-TiC Characteristics

FT-1Equivalent to Ferro-Tic CM. No softening at high temperature. Applying to wear-resistance parts, common tools, high-speed & high pressure molding, etc. Possible to use up to 600℃
Items : Rod Mill Guide Roller, Forming/Reducing/Pinch Roll, Punch
FT-2Equivalent to Ferro-Tic CS-40. Stainless 400 series. Corrosion resistance and high hardness
Items : Underwater Pelletizing Knife, Crimp Roll, Corrosion Resistance part.
FT-4Equivalent to Ferro-Tic C. Applying to tools, dies and wear parts. Excellent vibration damping ability in annealed condition.
Items : Vibration Absorption & Wear Resistance parts-Boring bar, Grinding Quill
FT-5Equivalent to Ferro-Tic HT6A. Strong resistance to deformation to temperatures above 980 ° C at high pressures. Non-magnetic, string oxidation and corrosion resistance
Items : Hot Forging Die, Hot Coining Die, Die for Extrusion